Influence of Composite Inlay/Onlay Thickness on Hardening of Dual-cured Resin Cements

This investigation evaluated the effect of resin composite inlay/onlay thickness on the hardness of a group of eight dual-cure resin-based cements. Fourteen disc specimens measuring 6 mm in diameter and 2.5 mm thick were prepared from each of eight dual-cure cements: Adherence, Choice, Duolink, Enforce, Lute-It, Nexus, Resinomer and Variolink. Two specimens from each material were directly light-cured while the remainder of the specimens were light-cured through resin composite spacers varying in thickness from 1 mm to 6 mm. Curing through the spacers always resulted in a decrease in the Knoop hardness number. For some cements, hardness values were reduced by 50% or more when the resin composite spacer thickness was 4 mm or greater even when measurements were made one week after dual-curing. Low hardness values indicate the presence of a weak chemical-curing mechanism that may compromise cement quality in areas of the cavity not readily accessible to the curing light.

MeSH Key Words: dental bonding; inlays; resin cements/chemistry